SKIN-CORE STRUCTURE IN MESOPHASE PITCH-BASED CARBON FIBERS: CAUSES AND PREVENTION

注意:本論文已在Carbon, Vol. 36, No. 12, pp. 1719–1724, 1998發表
使用者請注明論文出處

YONG-GEN LU¨(呂永根) ,a,* DONG WU,b QING-FANG ZHA,a LANG LIU¨ a and
CHANG-LING YANGa
aInstitute of Coal Chemistry, Chinese Academy of Sciences, Shanxi, 030001 Taiyuan,
People's Republic of China
bDepartment of Chemical Engineering, Taiyuan University of Science and Technology, Shanxi,
030001 Taiyuan, People's Republic of China


Abstract:To prohibit skin-core structure from appearing in mesophase pitch based carbon fiber (CF) with a large diameter (30–50 mm), measures such as decreasing oxidation temperature, prolonging holding time and increasing the oxygen partial pressure in the oxidative atmosphere were taken. EPMA (electron probe X-ray micro-analyzer) was utilized to detect the oxygen content distribution along the diameter of oxidized pitch fiber (OF). The transverse structure of OFs and CFs was observed under a scanning electron microscope (SEM). It was found with certainty that the skin-core structure in CFs is caused by steep oxygen content gradient along the diameter of their OFs. The oxygen distribution in
OFs was controlled by the oxidative stabilization conditions. In this work, the CF whose precursor fiber had been oxidized at 240°C in a flow of pure oxygen for 10 hours exhibits no skin-core structure and possesses a high tensile strength. The kinetics of stabilization was also studied. It can be concluded that those factors which increase oxygen diffusion or depress oxidative reaction are effective in overcoming skin-core structure in CFs. ? 1998 Elsevier Science Ltd. All rights reserved.
Key words:A. Carbon fibers, mesphase, B. EPMA, D. Diffusion.

1瀏覽PDF格式全文需要使用軟件--Abode Acrobat(由于軟件較大并常見,我站不提供下載)

2、下載論文全文請點擊鼠標右鍵“另存為”或使用斷點續傳軟件下載(358KB)


本站收錄的本文作者的其他論文:

1、Preparation of Porous Carbon Microspheres

2、Preparation of mesocarbon microbeads from coal tar

3、用稱重法研究聚丙烯腈樹脂的凝固過程

 更多相關論文請點擊本站的<<<站內全文搜索>>>查找

 

歡迎您參加討論,發表您對此論文及其研究領域的看法!
(請在發言時在標題中使用所點評的論文的題目或研究方向,這樣方便大家瀏覽!)

返回首頁 | CIMS論文 | 并行工程 | 虛擬制造 | 敏捷制造 | 其他論文 | 項目開發 | 學術資源 | 站內全文搜索 | 免費論文網站大全 |

line.gif (4535 字節)

為了更好的為大家服務,歡迎您參加本站的投票調查

>>>>參加更多投票調查請點擊!

本站永久域名:http://www.sqvswk.live歡迎訪問

注意:本站內容未經書面允許不得轉載

All rights reserved, all contents copyright 2000-2019
本站自2000年3月總網頁訪問量為
pk10开奖记录直播