中間相瀝青碳微球的制備及其嵌鋰行為的研究

注意:本論文已在《宇航工藝材料 》2001,6:27-29發表
使用者請注明論文出處

李寶華 呂永根 李開喜 呂春祥 凌立成
( 中國科學院山西煤炭化學研究所煤轉化國家重點實驗室 太原 030001 )

摘要:以含0.46%~3.7%(質量分數)吡啶不溶物(H)的寶鋼煤焦油為原料,在450℃下自升壓熱縮聚制備中間相碳~ (MCMB),然后將其在700~C下進行碳化。應用SEM、恒電流充放電等技術研究了所得MCMB的表面物理形態及充放電性能。研究發現:隨原料中一次H含量的增加,MCMB的球徑逐漸減小;首次電容量從326 n ·h·g 增至425 m_4·h-g~,首次不可逆容量先增加而后減小,而首次亢放電效率先減小而后增加。
關鍵詞: 煤焦油,中間相碳微球,嵌握,碳材料

Preparation of Mesocarbon Microbeads and Its Performance of Lithium Insertion

Li Baohua Lv Yonggen Li Kaixi Lv Chunxiang Ling Licheng
( NationalKey.Iat~ratmy of CoalCortversiort,Insfi'alte 0fCoal Chemistry.,Ckhnese Academyof Science Taiyoan 030001)

Abstract:Coal tars with different pyridine insoluble(PI)content(0.46-3.7wt%)were used as raw materials to prepare mesocarbon microbeads(MCMB) at 450℃for 2 h under autoginous pressure.MCMB were then heat-treated at 700℃ for 1 h.Surface morphology of the MCMB was investigated by SEM and constant-current charge-discharge properties were studied.It was found that,with the primary PI content increasing,the diameters of MCMB decreased, the first discharge capacity increased from 326 mA. h.g-1 to 425 mA.h. g-1 and the first coulombic efficiencies decreased at the beginning and then increased.
Key words:Coal tar,Mesocarbon microbeads,Lithium insertion,Carbon

1瀏覽PDF格式全文需要使用軟件--Abode Acrobat(由于軟件較大并常見,我站不提供下載)

2、下載論文全文請點擊鼠標右鍵“另存為”或使用斷點續傳軟件下載(129KB)


本站收錄的本文作者的其他論文:

1、Preparation of Porous Carbon Microspheres

2、Preparation of mesocarbon microbeads from coal tar

3、用稱重法研究聚丙烯腈樹脂的凝固過程

4、摻磷酚醛樹脂炭嵌鋰性能研究

5、聚丙烯腈纖維在預氧化過程中的結構和熱性能轉變

 更多相關論文請點擊本站的<<<站內全文搜索>>>查找

 

歡迎您參加討論,發表您對此論文及其研究領域的看法!
(請在發言時在標題中使用所點評的論文的題目或研究方向,這樣方便大家瀏覽!)

返回首頁 | CIMS論文 | 并行工程 | 虛擬制造 | 敏捷制造 | 其他論文 | 項目開發 | 學術資源 | 站內全文搜索 | 免費論文網站大全 |

line.gif (4535 字節)

為了更好的為大家服務,歡迎您參加本站的投票調查

>>>>參加更多投票調查請點擊!

本站永久域名:http://www.sqvswk.live歡迎訪問

注意:本站內容未經書面允許不得轉載

All rights reserved, all contents copyright 2000-2019
本站自2000年3月總網頁訪問量為
pk10开奖记录直播