Effect of hydrophobic group in polymer matrix on porosity of organic and carbon aerogels from sol–gel polymerization of phenolic resole and methylolated melamine

注意:本論文已在《Microporous and Mesoporous Materials 》2003,(62): 17–27發表
使用者請注明論文出處
Rui Zhang 1, Wen Li1, Xiaoyi Liang1, Gangping Wu1, Yonggen Lu1,2,Liang Zhan1, Chunxiang Lu1, Licheng Ling1,2,
1)Key Laboratory of Carbon Materials, Chinese Academy of Sciences, Taiyuan 030001, PR China
2)State Key Lab of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, PR China

Abstract:Organic and carbon aerogels were prepared by solution–sol–gel polymerization of phenolic resole and methylolated melamine followed by supercritical drying and pyrolysis. The hydrophobic group was incorporated into polymer matrix by adding m-cresol in the solution–sol–gel step and the effect of addition on porosity of organic and carbon aerogels was elucidated by nitrogen adsorption and density measurement. The ratios of m-cresol to phenolic resole (R) were changed from 0/7.5 to 2.5/7.5 while ratios of other components to phenolic resole remained unchanged. It is found that the total pore volumes of organic and carbon aerogels exhibit maxima at 1/7.5 and are determined by the total concentrations of reactants and cumulative volume shrinkages of gels from hydrogels to organic aerogels and from hydrogels to carbon aerogels respectively. The macropores in organic aerogels, developed in supercritical drying process, are determined by gel discrete particles–gel discrete particles interactions, which can be tuned by the incorporated hydrophobic groups. The micropores in carbon aerogels are generated by evolving volatile compounds in the pyrolysis process. The meso- and macropores in carbon aerogels are determined by (1) meso- and macropores in relevant organic aerogels; (2) volume shrinkages that convert macropores to mesopores and mesopores to micropores; (3) mass loss in pyrolyzing organic aerogels that increases sizes and volume of carbon aerogels; and (4) coarsening that converts mesopores to macropores to reduce interfacial energy. The mesopore size distributions of organic and carbon aerogels exhibit maxima at 1/7.5, which is also related to the actions of the hydrophobic groups. The BET surface areas of organic aerogels and external surface areas of carbon aerogels are determined by sizes and volumes of mesopores and the BET surface areas of carbon aerogels are determined by micro- and mesopores.
Keywords: Carbon aerogels; Pyrolysis; Adsorption; Density; Porosity

1瀏覽PDF格式全文需要使用軟件--Abode Acrobat(由于軟件較大并常見,我站不提供下載)

2、下載論文全文請點擊鼠標右鍵“另存為”或使用斷點續傳軟件下載(184KB)


本站收錄的本文作者的其他論文:

1、Preparation of Porous Carbon Microspheres

2、Preparation of mesocarbon microbeads from coal tar

3、用稱重法研究聚丙烯腈樹脂的凝固過程

4、摻磷酚醛樹脂炭嵌鋰性能研究

5、聚丙烯腈纖維在預氧化過程中的結構和熱性能轉變

6、中間相瀝青碳微球的制備及其嵌鋰行為的研究

 更多相關論文請點擊本站的<<<站內全文搜索>>>查找

 

歡迎您參加討論,發表您對此論文及其研究領域的看法!
(請在發言時在標題中使用所點評的論文的題目或研究方向,這樣方便大家瀏覽!)

返回首頁 | CIMS論文 | 并行工程 | 虛擬制造 | 敏捷制造 | 其他論文 | 項目開發 | 學術資源 | 站內全文搜索 | 免費論文網站大全 |

line.gif (4535 字節)

為了更好的為大家服務,歡迎您參加本站的投票調查

>>>>參加更多投票調查請點擊!

本站永久域名:http://www.sqvswk.live歡迎訪問

注意:本站內容未經書面允許不得轉載

All rights reserved, all contents copyright 2000-2019
本站自2000年3月總網頁訪問量為
pk10开奖记录直播